ZnSe Window
| Machinable shape | Circle, rectangle, polygon and other shapes |
| Size range | Diameter (maximum diagonal)：Φ8-Φ300mm |
| Thickness：0.05-50mm | |
| Fineness | 10-5 20-10 40-20 |
| Surface roughness | <5nm |
| Parallelism | <20″ |
| Coating | Customized according to customer requirements |
| Density（ g/cm3） | 5.27 |
| Melting point（℃） | 1525 |
| Resistivity Ω.CM | ~10^12 |
| Purity（%） | 99.9996 |
Physical Properties
| Coefficient of thermal expansion（1/℃） | 7.1*10^-6@273K |
| 7.8*10^-6@373K | |
| 8.3*10^-8@473K | |
| Thermal conductivity（J/k.m.s） | 18.0@298K |
| Heat capacity（J/g.k） | 0.339@298K |
| KnoopHardness(kg/mm2) | 110 |
| Bending strength（MPa） | 55 |
| Young modulus(GPa) | 67.2 |
| Poisson ratio | 0.28 |
Optical Properties
| Through wavelength range | 500nm-22000nm |
| Refractive index inhomogeneity（ΔN/N） | ＜3*10^-6@632.8nm |
| Absorption coefficient（1/cm） | 5.0*10^-3@1300nm |
| 7.0*10^-4@2700nm | |
| 4.0*10^-4@3800nm | |
| 4.0*10^-4@5250nm | |
| 5.0*10^-4@10600nm | |
| Thermal conductivity（J/k.m.s） | 1.07*10^-4@632.8nm |
| Heat capacity（J/g.k） | 7.0*10^-5@1150nm |
| KnoopHardness(kg/mm2) | 6.2*10^-5@3390nm |
| Bending strengt（MPa） | 6.1*10^-5@106000nm |
Zinc selenide window slice
| wavelength（nm） | Refractive index（n） | Refractive index（n） | wavelength（nm） |
| 620 | 2.5994 | 10600 | 2.4028 |
| 1000 | 2.4892 | 13000 | 2.3850 |
| 3800 | 2.4339 | 14600 | 2.3705 |
| 5000 | 2.4295 | 16600 | 2.3487 |
| 7000 | 2.4218 | 17800 | 2.3333 |
| 9000 | 2.4122 | 18200 | 2.3278 |
Website of this article：http://www.longsee-laser.com/en/ZnSe/7.html